Pengaruh Variasi Presentase HCL Terhadap Laju Korosi, Nilai Kekerasan dan Struktur Mikro Sambungan Las TIG Baja ST 60
Abstract
The purpose of this study was to determine the effect of variations in the percentage of HCL on the rate of corrosion. corrosion, to determine the effect of variations in current strength on the hardness value and microstructure of ST 60 steel. This study used an experimental method including the preparation of tools and materials, specimen making, welding process and corrosion rate testing, micro hardness vicker hardness. Then the highest corrosion rate value was obtained. of 3.6873996123 mm/year. The highest hardness value is at a current of 140 A in the weld metal area with a hardness value of 242.3 HV and the lowest hardness value is at a current of 120 A in the base metal area of 169.5 HV. The conclusion in this study is that the higher the current, the lower the corrosion rate will be inversely proportional to the hardness value, where the higher the amperage, the harder the hardness value
References
Dr.Ir Harsowono, T.Okomura “ Teknologi Pengelasan Logam “, JSSC, 1977.
T.K.R, Chamberlain. J..”Korosi Untuk Mahasiswa dan Rekayasawan”. 199
H.Iriandoko, dkk ,” Pengaruh heat treatment baja ST 60 terhadap nilai kekerasan dengan media pendingin asam cuka, ” 2020 ( Online)tersedia https://proceeding.unpkediri.ac.i d/index.php/inotek/article/view/ 144.
D.Prayitno,dkk “Pengaruh kuat arus pengelasan GTAW terhadap laju korosi baja karbon rendah, ” 2018 (Online) tersedia https://journal.uny.ac.id/index.php/dynamika/article/view/19109/10587.
A.P BayusenO,dkk,”Analisa korosi erosi pada baja karbon rendah dan sedang akibat aliran air laut, ” 2012 (Online) tersedia http://eprints.undip.ac.id/41570/.
G.AYudi,dkk “Analisa laju korosi baja ST 60 pasca proses las GTAW arus 80, 100, 120 Celcius,”2019 (Online) tersedia
https://publikasiilmiah.unwhas.ac.id/index.php/MOMENTUM/article/download/2660/2621.
Septianingsih,dkk “Pengaruh variasi konsenterasi asam klorida terhadap laju korosi baja karbon rendah ASTM A 139 tanpa dan dengan inhibitor kalium kromat, ” 2019 (Online) tersedia https://fmipa.unila.ac.id/wp- content/uploads/2019/08/CV- Ediman-Ginting-2019.pdf
.A Wibowo,dkk “Pengaruh kadar salinitas air terhadp laju korosi baja ST 60, ” 2021 (Online) tersedia https://repomhs.ulm.ac.id/handle/123456789/31237.
M.Z Yahya “Pengaruh vairasi arus dan kecepatan gas pelindung pada pengelasan material SS- 304 menggunakan las TIG terhadap kekuatan tarik dan struktur mikro, ” 2021 (Online) tersedia view/38447+&cd=1&hl=id&ct= clnk&gl=id.
S.Ninien, dkk “Analisa pengaruh variasi besaran arus las TIG terhadap perubahan struktur mikro,”2011 (Online) tersedia https://jurnal.polban.ac.id/ojs-,1,2/mesin/ article/ view/22.
D.Perdana, “Analisa pengaruh variasi arus pengelasan GTAW pada material plat SS 400 disambung dengan material plat SUS 304 terhadap sifat mekanis, ”2016 (Online) tersedia https://journal.itny.ac.id/index.php/ReTII/article/view/456.
F.Panundra “Pengaruh variasi kuat arus terhadap kekuatan tarik sambungan las tig semi otomatis, ” 2022 (Online) tersedia https://media.neliti.com/media/publications/145891-ID-analisa- pengaruh- pengelasan-tig-dan-mig.pdf.
Dr.Ir Harsowono, T.Okomura “Teknologi Pengelasan Logam“JSSC, 1977.
B. E. Putra, "Mengidentifikasi Welding Procedure Specification(WPS),"2018.
M.Z Yahya, “Pengaruh variasi arus dan kecepatan gas pelindung pada pengelasan material SS-304 menggunakan las TIG terhadap kekuatan tarik dan struktur mikro, “2021 (Online) tersedia view/38447+cd=1&hl=id&ct=clnk&gl=id.
S.Simbolon,dkk “Analisis sifat mekanik hasil pengelasan baja karbon rendah ST 42 dengan metode las TIG, ” 2021 (Online) tersedia http://openjournal.unpam.ac.id/index.php/JIPT/article/view/12761/7546.
J.M Kolo,dkk “Pengaruh variasi arus terhadap kekuatan impak dan kekerasan material ST 37 proses las GTAW,” 2017 (Online) tersedia https://www.researchgate.net/pub lication/346399311